welding-alloys.com 11 Typical mechanical properties Description and applications Other Rp0.2% [Mpa] Rm [Mpa] A5 [%] CVN [J] - 510 570 25 -40 °C: 70 Joining of base metal S235 to S355, P235 to P355, X42 to X60. Dedicated for use in construction, boiler plates, pipes, shipbuilding. - 510 580 26 -60 °C: 80 Recommended for welding of heavily worked or restrained joints with toughness required down to -60 °C. Joining of base metal S235 to S355, P235 to P355, X42 to X65. Dedicated for use in construction, boiler plates, pipes, shipbuilding, casting parts made of carbon manganese steel. - 480 580 28 -60 °C: 100 Welding of thick joints and safety-critical joining applications on high carbon, high sulphur or high phosphorus steels, under heavy static or dynamic stresses down to -60 °C. Joining of base metal S235 to S355, P235 to P355, X42 to X65. Dedicated to construction, boiler plates, pipes, shipbuilding, casting parts made of carbon manganese steel. - 540 610 27 -60 °C: 80 Deposition of cold tough steel alloyed with 1% nickel to improve toughness down to -60 °C. High resistance to cracking, thanks to a low amount of diffusible hydrogen guaranteed (<4 ml/100 g). Joining of base metal S275 to S460, P235 to P460, X42 to X65. Dedicated for use in construction, boiler plates, pipes, shipbuilding. - 520 600 24 -60 °C: 80 Mo: 0.3 610 720 24 -50 °C: 80 Deposition of steel alloyed with nickel and molybdenum to improve yield strength and toughness. Joining of base metal S355 to S550, P460, X60 to X70. Ideally suited for use in construction, oil and gas, shipbuilding. Mo: 0.4 600 680 24 -60 °C: 55 Mo: 0.5 760 820 17 -40 °C: 60 Deposition of steel alloyed with nickel and molybdenum to improve yield strength and toughness. Joining of base metal S500 to S690, P500 to P590, X70 to X80. Ideally suited for use in construction, oil and gas, shipbuilding. Mo: 0.5 760 850 20 -50 °C: 60 Back to contents page
RkJQdWJsaXNoZXIy Mjk4MDU2NA==